Zn - Zinc

Usually a grey colored transition metal, zinc was known in ancient Asia and early Europe. It can be easilly alloyed with copper and other metals and so has found wide metalurgical use. Lately zinc gluconate has become popular as a cold remedy.

Atomic number - 30 Density g/mL 7 .14

Atomic weight u 65 .38 Melting point K 692 .73

Bonding radius A 1 .25 Boiling point K 1180

Atomic radius A 1 .53 Heat of vaporization kJ/mol 115 .3

Ionization Potential V 9 .394 Heat of fusion kJ/mol 7 .322

Electronegativity - 1 .65 Specific heat J/gK 0 .39

The oxide is amphoteric.
Crystal are hexagonal.

Electron config. : [Ar] 3d¹⁰ 4s²

Isotopes of Zn: Click mass number for decay process, product for element page.

057 40 msec EC/ECp,14.620 Cu-57/Ni-56 56.964905	058 65 msec EC,9.370 MeV Cu-58 57.954599	059 182.0 msec EC/ECp,9.090 Cu-59/Ni-58 58.949264	060 2.38 min EC,4.158 MeV Cu-60 59.941832	061 89.1 sec EC,5.637 MeV Cu-61 60.939513	062 9.186 hr EC,1.627 MeV Cu-62 61.934333	063 38.47 min EC,3.367 MeV Cu-63 62.933215
064 48.6% Stable 63.929146	065 244.26 da EC,1.351 MeV Cu-65 64.929244	066 27.9% Stable 65.926036	067 4.1% Stable 66.927130	068 18.8% Stable 67.924847	069 56.4 min B-,2.675 MeV Ga-69 68.926553	070 0.6% 5E+14 yr ,6.739 MeV 69.925324
071 2.45 min B-,2.813 MeV Ga-71 70.927726	072 46.5 hr B-,8.220 MeV Ga-72 71.926863	073 23.5 sec B-,4.290 MeV Ga-73 72.929779	074 95.6 sec B-,2.340 MeV Ga-74 73.929457	075 10.2 sec B-,6.000 MeV Ga-75 74.932935	076 5.7 sec B-,4.160 MeV Ga-76 75.933397	077 2.08 sec B-,7.270 MeV Ga-77 76.937090
078 1.47 sec B-,6.440 MeV Ga-78 77.938571	079 0.995 sec B-/B-n,9.090 Ga-79/Ga-78 78.942672	080 0.545 sec B-/B-n,7.290 Ga-80/Ga-79 79.944411	081 0.29 sec B-/B-n,11.900 Ga-81/Ga-80 80.950509	MASS abund. Halflife Particle, Energy Decay Product(s) Isotopic Mass

Atomic number	-	30		Density	g/mL	7	.14
Atomic weight	u	65	.38	Melting point	K	692	.73
Bonding radius	A	1	.25	Boiling point	K	1180
Atomic radius	A	1	.53	Heat of vaporization	kJ/mol	115	.3
Ionization Potential	V	9	.394	Heat of fusion	kJ/mol	7	.322
Electronegativity	-	1	.65	Specific heat	J/gK	0	.39
The oxide is amphoteric.				Crystal are hexagonal.
Electron config. : [Ar] 3d¹⁰ 4s²